Waldent Alchem Nanoflow Zirconium Flowable Composite Shade

• It has high radiopacity and mechanical strength
• Superior wear resistance
• High filler load
• Flowable consistency
• Low shrinkage
• Excellent colour stability
• Excellent flexural strength.

Waldent Alchem Nanoflow Zirconium Flowable is an excellent flowable composite that delivers high strength & wears resistance. It is characterized by optimum surface affinity and penetrates easily into the most difficult areas. It combines esthetics as well as flow-on-demand handling for use.

Indications:

Waldent Alchem Nanoflow Zirconium Flowable

• Indicated for direct filling of class V (Cervical Caries)
• Root erosions
• Wedge-shaped defects
• Fillings of anterior teeth (Class III & IV)
• Small fillings in posterior teeth
• Block out of undercuts

• Diametric Tensile Strength 52,4 MPa
• Degree of conversion 83%
• Flexural modulus 12,6 GPa
• Shrinkage forces 0,91 MPa
• Diamond pyramid hardness 78 kg/mm²
• Thermal expansion coefficient 22 µm/m°C
• Flexural strength Nanoflow composite – 85 Mpa
• Compressive strength Nanoflow composite – 200 Mpa

• 1 x 2gm Syringe
• 4 x Dispensing Tips

• Isolation: A rubber dam is the preferred method of isolation.
• Cavity preparation: Prepare cavity with minimal tooth reduction.
• Apply Etchant Gel to enamel and dentin surfaces for 15 seconds. Rinse thoroughly for 15 seconds with water.
• Dry with clean, oil-free, air without desiccating the dentin.
• Do not allow the etched surface to become contaminated with saliva or blood during the bonding procedure.
• Adhesive: Immediately after blotting, apply 2-3 consecutive coats of adhesive to etched enamel and dentin for 15 seconds with gentle agitation using a fully saturated applicator. Remove excess solvent by gently drying with dry air for at least 5 sec to ensure a uniform glossy surface. Light cure for 20-30 seconds.
• Apply the material with the applicator tip directly in the cavity and pre-contour with a suitable instrument.
• The layer should not be thicker than 2mm.
• Light cure for 40 sec using a standard curing light.